PVI ANTISCORCHING Rubber Chemicals

0
No votes yet

Product Qty Per Unit: 
25.00
Product usage unit: 
Kg

Negotiate Price

Product Delivery Locations: 
Visakhapatnam, Vijayawada, Kakinada, Gangavaram, Krishnapatnam, Rawa, Nellore, Rajahmundry
Category: 
Rubber Chemicals-93

Retarder agent Rubber Chemicals

Product Description: 

PVI is an effective scorch inhibitor with almost all types of accelerators and in all types of sulphur cured diene rubber based compounds.
Crystaline Powder

Product Application: 

PVI is an ideal pre vulcanization (scorch) inhibitor for NR, IR, NR-BR blend, SBR, NR-SBR, SBR-BR blends, NBR, CR and other diene rubber based accelerated sulphur cured compounds.

The product may be used in natural rubber and synthetic rubber. It may protect effectively the rubber material from scorching during Processing, So that to make it possible for extruder and calender to be running at a high temperature and high speed and improve the production capacity of vulcanizer. The product also can improve the storage stabilization of the rubber material, protect natural vulcanization during storage. It has reclaimaion function for rubber material, which bearing high heating or with dangers of scorching.

Product Procedure: 
In general PVI Retarders can be 0.5 to 1.50 phr
PVI can be used effectively in compounds based on NBR/PVC blends, polyacrylic rubbers and sulphur cured polyurethanes.

PVI is most effective at sulphur dosages between 1.5-3.0 phr and it is not effective with organic peroxide, PF resin and metal oxide cure
Product Note: 

PVI does not cause any detrimental effect on the vulcanizate properties such as tensile strength, modulus values, and resilience / heat build up, compression set or permanent set, ozone resistance and hot air aged vulcanizate properties when used at optimum dosage.

PVI does not cause contact or migration staining but can slightly discolor bright white rubber products.

PVI can permit addition of curatives at an early stage of mixing for better dispersion of curatives, reduced mixing cycle time, reduced power consumption, reduced labor and capital investment costs.

PVI use of higher processing speeds and temperatures during mixing, calendaring, extrusion, etc. for increased productivity and reduced processing cost.

PVI use of higher injection temperatures and shorter cure cycles for increased productivity.
PVI recovery of rubber compounds with marginal processing safety and recovery of partially scorched compound for scrap elimination.

PVI improve the storage stability of fully compounded stocks at ambient temperatures.

Product Technical Specification: 

Composition Specification: N-(Cyclohexylthio) phthalimide
Melting Point : 90-95 Degree C

 

Item 

Specification 

Appearance 

White or Light yellow powdered crystal 

Available composition content 

96% Min. 

Melting point 

89 -94°C 

Heating loss 

0.50% Max 

Ash content 

0.10% Max 

Residue(150um) 

0.0% Max 

Identification IR 

Identical to standard 

 
Product pack size: 
Crystaline Powder 20 / 25kg Poly lined poly woven bag / Poly lined paper bag. It is white or yellow crystalline. It can be dissolved in acetone, benzene, toluene, ethyl ether and ethyl acetate as well as warm carbon tetra chloride, ethyl alcohol and heptane. It also can be slightly dissolved in gasoline, but not in kerosene and water.
Product alias: 
Article: 
Remarks: 

Chemical name: N-(cyclhexyl thio) phthalimide 
Molecular Formula: C14H15O2NS 

SKU:
RXSOL-93-9301-025
Title:
PVI ANTISCORCHING Rubber Chemicals