Anti Corrosive Agent
RXSOL ANTI CORROSIVE AGENT is a solvent cutback, wax base, general purpose, corrosion preventive compound.RXSOL ANTI CORROSIVE AGENT is excellent for long term protection of metallic surfaces against corrosion in either indoor or outdoor exposure and during domestic and international shipments, like machinery, machine rolls/tools, automatic parts, dies, tubing, and spare parts.RXSOL ANTI CORROSIVE AGENT cures to a dark amber colored, waxy, transparent, firm film.
RXSOL ANTI CORROSIVE AGENT is formulated to be used as supplied. Ensure uniform consistency prior to use. Continued stirring is generally not required. If the product thickens due to cold storage or loss of solvent during use, contact Valvoline. DO NOT THIN RXSOL ANTI CORROSIVE AGENT. Incorrect thinning will affect film build, dry time and product performance.Rx Marine International recommends that the ambient and product temperature be 10-35 °C at the time of product application.RXSOL ANTI CORROSIVE AGENT can be applied by airless spray or brush.
Net Materials by spray machine or Brush.
Removal:
RXSOL ANTI CORROSIVE AGENT can be removed with mineral spirits or any similar petroleum solvent, hot alkaline wash or low pressure steam.
Storage:
RXSOL ANTI CORROSIVE AGENT should be stored at temperatures between 10-35 °C. Mild agitation is recommended prior to use. Due to its composition RXSOL ANTI CORROSIVE AGENT can be subject to postproduction viscosity changes during storage.Under proper storage conditions RXSOL ANTI CORROSIVE AGENT can have a shelf life of 4 years minimum.
Caution:
Adequate ventilation is required for cure and to ensure against formation of combustible liquid. THE PARTIALLY CURED FILM SHOULD NOT BE EXPOSED TO IGNITION SOURCES SUCH AS FLARES, FLAMES, SPARKS, EXCESSIVE HEAT OR TORCHES. Refer to Material Safety Data Sheet for additional handling and first aid information.
Note:
The addition of any product over or under this coating is not recommended. The use of additional coatings could result in chemical incompatibility, thus affecting the performance of this coating as stated in the Typical Properties section.
Typical Properties
| Flashpoint; PMCC | 40 | °C |
| Specific Gravity @ 60°F | 0.87 | kg/ltr |
| Recommended Dry Film Thickness | 50 | microns minimum |
| Theoretical Coverage @ Avg. Recommended DFT | 9.2 | m²/l |
| Non Volatile | 52 | weight % |
|
Viscosity; DIN (53 211) Cup No. 4 @ 20°C (at time of manufacture) |
85 | seconds |
| Dry to Touch Time @ 25°C | ± 2 | hours |
| Cure Time @ 25°C | ± 24 |
hours |
| Volatile Organic Content (VOC) (ASTM D-3960) | 415 | g/l |
Accelerated Corrosion Tests:
@ Avg. Recommended DFT
| Salt Spray; 5 % NaCl @ 35°C; DIN 50 021 (ASTM B-117) (DIN 1623 Steel Panels) | 40+ |
days |
| Humidity; 100 % RH; @ 40°C; DIN 50 017-KK (DIN 1623 Steel Panels) | 100+ |
days |